Titanium Grade 11 |
Chemical composition (weight %) (Maximum values unless range is shown) |
O |
N |
C |
H |
Fe |
Pd |
V |
Ni |
Mo |
Others |
Residuals |
0.18 |
0.03 |
0.10 |
0.015 |
0.20 |
0.12-0.55 |
| |
|
|
0.4 |
This alloy is the same as Grade 1, but with Pd for better corrosion resistance. Grade 11 has optimum ductiility and cold formability. It has also useful strength, high-impact toughness and excellent weldability.
|
Mechanical properties at room temperature |
|
Minimum values |
Typical values |
Yield Strength |
170 MPa |
220 MPa |
Ultimate Strength |
240 MPa |
345 MPa |
Elongation in 50 mm, A5 |
25% |
37% |
Reduction in Area |
35% |
% |
Hardness |
. |
120-150 HV |
Modulus of elasticity |
. |
103 GPa | |
|
|
|
|
|
|
|