Titanium Grade 6 |
Chemical composition (weight %) (Maximum values unless range is shown) |
O |
N |
C |
H |
Fe |
A1 |
V |
Sn |
Mo |
Others |
Residuals |
0.20 |
0.05 |
0.08 |
0.02 |
0.50 |
4.0-6.0 |
| 2.0-3.0 |
|
| 0.4 |
An alloy for airframe and jet engine applications requiring good weldability, stability and strength at elevated temperatures.
|
Mechanical properties at room temperature |
|
Minimum values |
Typical values |
Yield Strength |
795 MPa |
900 MPa |
Ultimate Strength |
825 MPa |
970 MPa |
Elongation in 50 mm, A5 |
10% |
16% |
Reduction in Area |
25% |
% |
Hardness |
. |
330-350 HV |
Modulus of elasticity |
. |
110 GPa |
Charpy V-Notch Impact |
. |
14 J | |
|
|
|
|
|
|
|